Moulding process of composite material including high-thermal &amp; shy; conductor and room-temperature magnetic refrigerant

ABSTRACT

A molding process of composite material including high-thermal-conductor and room-temperature magnetic refrigerant comprises the steps of nesting magnetic refrigerant with high-thermal-conductor and connecting them mutually, especially making the room-temperature magnetic-thermal-conductor into sheet, strip or filament, inserting the high-thermal-conductors&#39;sheet, strip or filament in the room-temperature magnetic refrigerant&#39;s sheet or filament and connecting them fully. This invention has solved the application of the room-temperature magnetic-thermal-conductor, particularly the application of the room-temperature magnetic-thermal-conductor which is lower thermal-conductor, easier oxidation and powdering. The invention utilizes the high thermal-conductor to solve the problem of room-temperature magnetic refrigerant which is poor in conventional heat exchange, meanwhile decreases the loss of the magnetic-thermal effect.

1. FIELD OF INVENTION

This invention relates to a molding process of a kind of refrigerant material. It also relates to a method and an apparatus to increase the heat transfer, more specifically, it relates to a molding process of composite material including room temperature magnetic refrigerant material. The process reorganizes the magnetic refrigerant material and high-thermal-conductor to make the composite material. The invention can also be utilized to make the magnetic cold storage material in low temperature chillers.

2. DESCRIPTION OF THE RELATED ARTS

Since around one third of the world's energy is consumed by refrigeration, the progress of refrigeration technology is very important to the survival of human beings. The main refrigeration technologies include evaporation refrigeration, gas expansion refrigeration, absorption refrigeration, thermal electric refrigeration, vortex tube refrigeration, thermal sound refrigeration, pulse tube refrigeration, magnetic refrigeration, etc. The prevalent technology is evaporation refrigeration. This kind of technology requires the use of freon which not only destroys the ozone layer, but also induces the green-house effect. So, refrigeration directly affects the energy consumption and the environment. The research and development of a new type of energy-saving and environment-friendly refrigeration method is becoming imminent and of great significance.

Magnetic refrigeration was confirmed scientifically in 1926. In theory, it has the highest circulation efficiency without a compressor, therefore, it became the dream refrigeration method for many physicists. Unfortunately, the later research and development only succeeded in the ultra low temperature (around absolute zero) and the research and development came to a halt after many failures in room temperature magnetic refrigeration. Differing from the magnetic refrigeration at low temperature, the circulation mode, the magnetic material and magnetic field of room temperature magnetic refrigeration require special consideration and the room temperature magnetic refrigeration is difficult to carry out.

In 1976, Brown of NASA utilized gadolinium plate added with alcohol water mixture as the refrigerant and accomplished a 38° C. temperature difference for the first time in a super-conductive magnetic field. This achievement showed the possibility of room temperature magnetic refrigeration.

In 1982, Barclay and Clayart of the United States proposed the new concept of Active Magnetic Refrigeration (AMR) which laid the theoretical foundation of practical room temperature magnetic refrigeration.

In 1990, the United States Department of Energy sponsored NASA and Ames Laboratory of Iowa State University to develop a room temperature magnetic chiller prototype based on AMR. During the search of material for room temperature magnetic refrigeration, they found that the gadolinium-silicon-germanium alloy has a magnetic-thermal effect much greater than pure gadolinium. After 8 years of hard work on the research of room temperature magnetic chiller, in 1997, the first high efficiency and durable reciprocating type of room temperature magnetic chiller came out. It applied a metal gadolinium ball, with the diameter of 0.1 mm-0.3 mm, as the refrigerant. The refrigerant weighed 3 kilograms. The magnetic field applied was 1.5-5 tesla with the cycle time of 6 seconds. The chiller was operated for 1500 hours. While the chiller was operated in the magnetic field of 5 tesla and 1.5 telsa, its thermal dynamic perfection rate was 60% and 20% respectively. This chiller predicted the coming of a new era of room temperature refrigeration technology.

Room temperature magnetic refrigeration is the way of the future refrigeration. It will inevitably replace the current refrigeration methods. All air conditioners, refrigerators and other types of chillers will be transformed in a revolutionary way. Currently, the primary concern of the room temperature magnetic refrigeration is efficiency, reliability and cost. With the perfection of room temperature magnetic refrigeration technology, the product structure of the refrigeration industry of the world will undergo a significant change and the market potential for room temperature magnetic refrigeration is huge. Since 1997, practical feasibility study of room temperature magnetic refrigeration has started. As the competing and reference standard of room temperature magnetic refrigeration is the conventional steam compressed type refrigeration. It requires that the room temperature magnetic refrigeration must not only be cost effective, but also compact with high operating efficiency. These objectives can be achieved by increasing the operating speed, using room temperature magnetic refrigerant with greater magnetic-thermal effect and increasing the magnetic field intensity. Since technology will continue use fluid to facilitate the heat exchange with the room temperature magnetic refrigerant material, there is the need for molding such material. This invention is directed at the molding process of room temperature magnetic refrigerant material for the room temperature magnetic refrigeration technology.

3. DETAILED DESCRIPTION OF THE INVENTION

This invention provides a molding process and apparatus of composite material including magnetic refrigerant to increase the refrigeration capacity of room temperature magnetic refrigeration, improve the heat transfer, reduce the oxidation rate of the material, and improve its operation life. The purpose of this invention also includes the increase of the refrigeration capacity and efficiency of room temperature magnetic refrigeration by magnification. Room temperature magnetic refrigerant material is a material with magnetic-thermal effect. Typically it includes gadolinium metal, Dy—Al alloy, Gd—Si—Ge alloy, Mn—Fe—P—As alloy, La—Fe—Si alloy, etc. It also includes the ceramic type of room temperature magnetic-thermal effect material, such as La—Ca—Mn—O material with the structure of Ca—Ti ore and a working temperature of 20-330 K.

The main feature of this invention is to nest a room-temperature magnetic refrigerant material with a high-thermal conductor or vise versa to make the composite material including high-thermal-conductor and room-temperature magnetic refrigerant material.

The high-thermal-conductor in this invention includes artificial crystal, ceramics, etc. Under special circumstances, diamond powder can also be used.

The first method is an embedding method. The room temperature magnetic refrigerant material is processed to tiny balls of appropriate size by cutting, crushing, ball grinding, plasma spray coating and other mechanical processing methods. The minimum size of the balls shall be more than 0.001 mm, and the irregularity of the shape shall be within the scope of this invention. The detailed process is described as follow:

1. The high-thermal-conductor, such as aluminum, copper or silver which has lower melting point than that of the room temperature magnetic refrigerant material, is heated to its melting point and becomes liquid under the vacuum or in the inert atmosphere (no vacuum or inert atmosphere is needed if the conductor's oxidation potential is low), then the room temperature magnetic refrigerant material in the shape of tiny balls is added into the molten high-thermal-conductor. If the melting point of the magnetic refrigerant material is lower than that of the high-thermal-conductor, then the process shall be reversed (processing the high-thermal-conductor into tiny balls and adding them into the molten magnetic refrigerant material).

2. Cool the resulting liquid (usually metal liquid) from step 1 under vacuum or in inert atmosphere to solid. The inner structure of the composite obtained is similar to the inner structure of concrete with cement and rubbles.

3. Machine the solid to particles, such as tiny balls, with various shapes and the diameter of less than 1 mm; sheets with the thickness of less than 1 mm; or filament with diameter of less than 1 mm.

4. If the particle shaped composite material is susceptible to oxidation, a layer of oxidation proof metal may be plated. The resulting composite particles are then placed into the room temperature magnetic chiller and make them compact so that the room temperature magnetic refrigeration can be carried out.

5. If the particles in step 4 are of filament shape, the diameter of the filament shall be more than 0.001 mm.

As another aspect of this invention, the room temperature magnetic refrigerant is made by stacking the sheet units of the room temperature magnetic refrigerant material and creating the salient points between the sheet units to form the liquid path.

The sheet unit described above is comprised of two metal sheets with a liquid thermal conductive agent filled in between. Said liquid thermal conductive agent includes super-paramagnetism and ferromagnetism room temperature magnetic refrigerant particles. Said two metal sheets are divided into several small isolated areas by completely pressing together the two metal sheets at designed points.

The diameter of the super-paramagnetism or ferromagnetism room temperature magnetic refrigerant particles is greater than 0.0001 mm.

The thickness of the said sheets is less than 0.1 mm, and the thickness of sheet units is less than 1 mm or thinner.

The height of the salient points is no more than the thickness of the sheet units.

To ensure the free flow of the liquid in the liquid path between the sheets, a metal powder with the diameter of 0.1-1 mm is spread between the sheets.

The metal sheets described above are copper sheets or other metal sheets with high thermal conductivity.

The thickness of the stacked sheet units is between 1 mm and 100 mm with the fluid path between the sheet units.

The detailed process for making the room temperature magnetic refrigerant is described as follow: crush, ball grind, plasma spray coat or machine the super-paramagnetism or ferromagnetism room temperature magnetic refrigerant material into powder with the particle size not less than 0.0001 mm; prepare the metal sheets of thickness less than 0.1 mm; add the powder into the liquid thermal conductive agent and then seal the agent containing the powder between two metal sheets and compress them to form sheet units of thickness less than 1 mm; divide the compressed sheets into small isolated areas by completely pressing together the sheets at designated points; stack the sheet units; and create salient points between the sheet units to form the liquid paths. The said metal sheets are copper sheets or other metal sheets with high thermal conductivity. The height of the salient points is no more than the thickness of the sheet units. A metal powder with the diameter of 0.1-1 mm is spread between the sheet units. The thickness of the stacked sheet units is between 1 mm and 100 mm.

The molding process of the composite material including room temperature magnetic refrigerant material in this invention also includes:

The room temperature magnetic refrigerant material, such as gadolinium metal and Gd—Si—Ge alloy, is machined to sheets. The thickness of the said sheets or diameter of the said filament is not more than 0.1 mm. A high-thermal-conductor sheet is inserted between the machined sheets of room temperature magnetic refrigerant material to form a sandwich structure.

The thickness of the high-thermal-conductor sheet is in the same order as that of the sheet of the room temperature magnetic refrigerant material and may vary depending on the type of material used.

The full and close contact is required between these two kinds of different sheets so that the heat of the room temperature magnetic refrigerant can be exchanged with the outside through high-thermal-conductor.

Further machine the composite material including room temperature magnetic refrigerant material to balls, sheets or other kinds of shapes. The thickness of the sheet composite material is less than 1 mm or much thinner. The size of other shapes of composite material shall also be less than 1 mm. Before the composite material is installed into the room temperature magnetic refrigerant chiller, it is surface treated to achieve oxidation proof.

Since the thermal conductivity coefficient of the room temperature magnetic refrigerant material, such as gadolinium, is much lower (several dozens times lower) than that of the high-thermal-conductor, the cycle time will be shortened enormously and the unit time refrigeration capacity will be increased significantly if the thermal conductivity coefficient of gadolinium can be increased significantly or the size of the material can be decreased. But there is a limit as to how small the size can be reduced to because the flow resistance of the heat exchange fluid increases significantly as the size decreases. Employing a material of the smallest size possible, we can strengthen the heat transfer design of the material. The new composite material can transfer the heat to the high-thermal-conductor. Although the single magnetic-thermal effect of such composite material is decreased during each cycle, the increase of the refrigeration capacity resulted from the shorter cycle time induced by high thermal conductivity far exceeds the decrease of the refrigeration capacity due to the decrease of the single magnetic-thermal effect. The typical structure of the composite material is shown in FIG. 2.

The advantages of this invention: The basic principle of room temperature magnetic refrigeration is to use the temperature effect of the magnetic material while entering and leaving the magnetic field. Since the temperature effect for each single cycle is relatively small, it is necessary to apply a technology, such as an active mode magnetic cold storage vessel, to magnify and accumulate such temperature effect. By using the active mode magnetic cold storage vessel, the magnetic material also acts as the cold storage vessel in addition to its function of refrigeration. It needs to exchange the heat with the outside to adjust the temperature change of the material.

This invention is also characterized as:

-   1. Successful application of the room temperature magnetic     refrigerant material for room temperature magnetic refrigeration,     particularly the application of room temperature magnetic     refrigerant material which has low thermal conductivity, is     susceptible to oxidation and brittle in room temperature magnetic     refrigeration. -   2. Isolation of room temperature magnetic refrigerant from the heat     exchange fluid to prevent the said refrigerant from being oxidized. -   3. Successful application of the high-thermal-conductor to solve the     problem of slow heat exchange of room temperature magnetic     refrigeration, while minimizing the loss of the magnetic-thermal     effect. The high thermal conductivity of the composite material can     significantly increase the speed of the refrigeration cycle, and     well compensate the negative impact on the refrigeration capacity     caused by the decrease of its magnetic-thermal effect. It is very     effective to use this material to increase the cycle speed of room     temperature magnetic refrigeration. Since the point contact is the     conduct mode of the composite material after the molding, under     intensified heat transfer (one order of magnitude higher than     normal), the heat loss between the high and low temperature source     is small

4. BRIEF DESCRIPTION OF DRAWINGS

FIG. 1 is the structural representation of the sheet units described in this invention;

FIG. 2 is the structural representation of the composite sheets described in this invention;

FIG. 3 is the cross section of structural representation of FIG. 2 in this invention; and

FIG. 4 is structural representation of the composite ball described in this invention.

5. EXAMPLES Example 1

The room temperature magnetic refrigerant is made by stacking the sheet units of the material which is 0.1 mm thick. The thickness of the stacked units is 5 mm. A truncated cone of 1 mm diameter and 0.05 mm height is inserted between the two sheet units at a 5 mm interval and the fluid path is so obtained. The sheet unit is comprised of two copper sheets of 0.01 mm thickness. A liquid oxidation resistant thermal conductive agent gallium is suffused therebetween. The liquid gallium stated above is dopped with room temperature magnetic refrigerant material gadolinium to form room temperature magnetic refrigerant. The diameter of the refrigerant is 0.005 mm. Impressions are made about every 3 mm between the two copper sheets to form the small isolated areas. The process is described in detail as below:

-   1. Machine the room temperature magnetic refrigerant material     gadolinium into sheets; or crush with water, ball grind, plasma     spray coat or machine the room temperature magnetic refrigerant     material gadolinium directly into gadolinium balls of suitable size     of more than 0.005 mm. -   2. Prepare copper sheets of less than 0.01 mm thick. -   3. Seal the room temperature magnetic refrigerant gadolinium balls     and oxidation proof thermal conductive agent gallium between the two     copper sheets. The gadolinium balls should be packed densely. The     material obtained as above is then compressed into a sheet unit with     the thickness of 0.1 mm. On the surface of the resulting sheet unit,     truncated cones of 1 mm diameter and 0.05 mm height are placed every     5 mm apart. At a 3 mm interval, the copper sheets are pressed     together completely to form small isolated areas between the copper     sheets. -   4. Stack the sheet units and fix them under pressure to obtain the     necessary mechanical strength. The pressure shall not be too high so     that a fluid path is obtained. The thickness of the stacked sheet     units is 5 mm. -   5. Cut the room temperature magnetic refrigerant obtained above to     desirable size to be applied in the room temperature magnetic     chiller. The structure is shown in FIG. 2 and FIG. 3.

Example 2

The structure and process of making the room temperature magnetic refrigerant is basically the same as described in Example 1, except that the room temperature magnetic refrigerant material used is a super-paramagnetic material with particle size of 0.001 mm; the thickness of the sheet units is 0.05 mm; the spherical metal powders, 0.05 mm in diameter, are dispersed between the sheet units and the thickness of the stacked sheet units is 90 mm.

Example 3

The room temperature magnetic refrigerant material is gadolinium and the thermal conductive metal is aluminum.

-   1. Mechanically crush the gadolinium to balls with appropriate size     of 0.025 mm in diameter. -   2. Melt the aluminum at 940 K under argon, and then place the     gadolinium balls obtained from step 1 into the molten aluminum. -   3. Compress the aluminum and the gadolinium balls at 940 K and then     cool it down. -   4. Machine or otherwise process the material obtained from step 3 to     small balls with 0.25 mm in diameter. It is shown in FIG. 4.

Example 4

As shown in FIG. 2, the molding process of composite material including high-thermal-conductor and room temperature magnetic refrigerant material comprises: cutting the room temperature magnetic refrigerant material such as gadolinium or Gd—Si—Ge alloy into sheets or filaments with section diameter less or much less than 0.1 mm; and inserting the high-thermal-conductor sheets or filaments of the similar size between the room temperature magnetic refrigerant material sheets or filaments to ensure full and close contact. The process includes: alternately stacking the room temperature magnetic refrigerant material gadolinium or Gd—Si—Ge alloy which is rolled into sheets with copper or aluminum sheets; compressing the stacked sheets; and, cutting them into sheets, strips or filaments. The heat of the room temperature magnetic refrigerant is mainly exchanged with outside through the high-thermal-conductor. As an aspect of this invention, the high-thermal-conductor is aluminum.

It is with difficulties to cut the composite material into sheets. This invention also provides a drilling method to make the end product. The method processes the stacked material into a honeycomb shape. Under the operating condition, heat exchange media flows in the honeycombed holes.

The thickness of gadolinium sheets is 5-100 μm and the thickness of copper sheets is of the same range. Gadolinium sheets alternates with copper sheets while being stacked together. The most optimal mode is to insert a aluminum foil between the gadolinium and copper sheets, compress the sheets and then heat the sheets to 934 K or above to melt the aluminum so that a closer contact between gadolinium and copper sheets can be achieved.

This invention is easy to carry out in the industry. 

1. A molding process of a composite material including a high-thermal-conductor and a room temperature magnetic refrigerant material, wherein said room temperature magnetic refrigerant material is nested with said high-thermal-conductor to obtain said composite material.
 2. The molding process of claim 1, wherein said room temperature refrigerant material is processed to particles, sheets or filaments of appropriate size by crushing, ball grinding, plasma spray coating or other machining methods to the minimum section size of more than 0.001 mm; said high-thermal-conductor is then embedded in said room temperature magnetic refrigerant material; if the melting point of said magnetic refrigerant material is lower than that of said high-thermal-conductor, said room temperature magnetic refrigerant material is embedded in said high-thermal-conductor.
 3. The molding process of claim 1, wherein said composite material is obtained by stacking multiple sheet units and creating salient points between said sheet units to form liquid paths; said sheet unit is comprised of two metal sheets and a liquid thermal conductive agent therebetween; said liquid thermal conductive agent includes super-paramagnetism or ferromagnetism room temperature magnetic refrigerant particles, sheets or filaments; and said sheet units are pressed completely together at designated points to form small isolated areas.
 4. The molding process of claim 1, wherein said room temperature magnetic refrigerant material is processed to sheets, strips or filaments; said high-thermal-conductor is inserted between said sheets, strips or filaments; and said high-thermal-conductor and the said sheets, strips or filaments contact each other closely.
 5. The molding process of claim 2, wherein the melting point of said high-thermal-conductor is different from that of said room temperature magnetic refrigerant material selected; melt said lower melting point high-thermal-conductor or room temperature magnetic refrigerant material under the vacuum or inert atmosphere; add said higher melting point room temperature magnetic refrigerant material or high-thermal-conductor therein; cool the metal fluid containing the higher melting point material under the vacuum or inert atmosphere to a solid; and machine said solid to small balls with diameters of less than 0.5 mm.
 6. The molding process of claim 3, wherein said super-paramagnetism or ferromagnetism room temperature magnetic refrigerant material is cut, crushed, ball grinded, plasma spray coated or processed by physical or chemical methods to particles with the particles size less than 0.0001 mm; prepare metal sheets, add said particles into a liquid thermal conductive agent, seal said liquid thermal conductive agent containing said magnetic refrigerant material between said two metal sheets and compress them to sheet units of thickness less than 0.1 mm; divide said sheets into small isolated areas by completely pressing together the said sheet units at the designated points, stack said sheet units and create salient points between said sheet units to form said liquid path; said sheets are comprised of copper; the height of the salient points is not more than the thickness of the sheet units and a metal powder with the particle size of 0.1-1 mm is spread therebetween; and the thickness of the stacked sheet units is between 1 mm and 100 mm.
 7. The molding process of claim 3, wherein the thickness of said sheets is less than 0.1 mm; the thickness of said sheet units is less than 0.2 mm; the thickness of said stacked sheet units is between 1 mm and 100 mm; and said fluid paths exist between said sheet units.
 8. The molding process of claim 3, wherein the height of said salient points is no more than the thickness of said sheet units; and a metal powder with the particle size of 0.1-1 mm is spread between said sheet units.
 9. The molding process of claim 4, wherein the thickness of a gadolinium sheets is 5-100 μm; the thickness of a copper sheet is 5-100 μm; and said gadolinium sheets and said copper sheets are stacked alternately together.
 10. The molding process of claim 4, wherein an aluminum foil is inserted between said gadolinium and copper sheet; the resulting stacked sheet is then compressed and heated to at least 934 K to melt said aluminum foil and to obtain a closer contact between said gadolinium and said copper sheet
 11. The molding process of claim 10, wherein said stacked sheets are processed to honeycombed shape.
 12. The molding process of claim 5, wherein the surface of said balls is plated a layer of oxidation proof metal. 